C19210 WIRE
C19210 WIRE
Standard
| JIS | DIN | EN | ASTM/UNS/CDA | GB/T |
| C1921 | CuFe0.1P | CuFe0.1P | C19210 | / |
Merit
C19210 is a micro-alloyed material belonging to the group of copper iron alloys. It has a very high conductivity combined with excellent cold forming properties. Softening resistance of low strength tempers is good.
Applications
It is a popular alloy for leadframes for power transistors and ICs, connector tabs, automotive battery clamps and components for the electrical industry.
| Cu | Remainder | |
| Fe | 0.05-0.15 | |
| P | 0.025-0.04 |
Request a Quote
| Temper | Diameter (mm) | Tensile Strength(Mpa)min | Tensile Strength(Mpa)max | Hardness(HV) | Bending Test(90°)GW | Bending Test(90°)BW |
| O | 0.4-1.6 | 220 | 335 | – | – | – |
| 1/2H | 0.4-1.6 | 260 | 440 | – | – | – |
| H | 0.4-1.0 | 335 | 510 | – | – | – |
| EH | 0.4-0.8 | 440 | – | – | – | – |
Physical properties of the above materials are conventional performance indicators.If you have some special requirements,(for example property and tolerance).please contact Kinmachi Company directly，we will give you professional assessments and answers.
| Density (g/cm³) | 8.9 |
| Electrical conductivility IACS%(20℃)* | 86 |
| Modulus of elasticity (KN/mm²) | 125 |
| Coefficient of thermal expansion 10-6/K | 17 |
| Thermal conductivity W/(m*K) | 350 |
*value for the lowest temper class
JIS: C1921
DIN: CuFe0.1P
EN: CuFe0.1P
UNS: C19210