C19210
C19210
Standard
| JIS | DIN | EN | ASTM/UNS/CDA | GB/T |
| C1921 | CuFe0.1P | CuFe0.1P | C19210
ASTM B465 |
/ |
Merit
C19210 is a micro-alloyed material belonging to the group of copper iron alloys. It has a very high conductivity combined with excellent cold forming properties. Softening resistance of low strength tempers is good.
Applications
It is a popular alloy for leadframes for power transistors and ICs, connector tabs, automotive battery clamps and components for the electrical industry.
| Cu | Remainder |
| Fe | 0.05-0.15 |
| P | 0.025-0.04 |
Request a Quote
| Temper | Tensile Strength(Mpa) | Yield Strength(Mpa) | Elongation (%) | Hardness(HV) | Bending Test(90°)GW | Bending Test(90°)BW |
| R300 | 295-380 | max. 300 | min. 10 | 80-110 | 0 | 0 |
| R360 | 360-440 | min. 260 | min. 3 | 100-130 | 0 | 0 |
| R420 | 415-500 | min. 350 | min. 2 | 120-150 | – | – |
Physical properties of the above materials are conventional performance indicators.If you have some special requirements,(for example property and tolerance).please contact Kinmachi Company directly，we will give you professional assessments and answers.
| Density (g/cm³) | 8.9 |
| Electrical conductivility IACS%(20℃)* | 86 |
| Modulus of elasticity (KN/mm²) | 125 |
| Coefficient of thermal expansion 10-6/K | 17 |
| Thermal conductivity W/(m*K) | 350 |
*value for the lowest temper class
JIS: C19210
DIN: CuFe0.1P
EN: CuFe0.1P
UNS: C19210 ASTM B465